我叫杜大力，是中国科学院大学宁波材料所海洋新材料与应用技术重点实验室2021级研究生，主要从事耐高温腐蚀涂层的设计，以及高温防护涂层的耐腐蚀以及抗氧化机理探究探索。

　　文章链接：https://doi.org/10.1016/j.corsci.2023.111406

　　该论文《NaCl-induced hot-corrosion behavior and mechanism of TiSiCN/Ag nanocomposite coatings by arc ion plating》发表于Corrosion Science，中科院JCR分区为一区Top期刊，影响因子8.3。在文章我们使用贝意克的管式炉设备，论文原文如下：The hot corrosion test of the substrate and coating samples were performed in a high temperature tube furnace (Beq BTF-1200 C-III, Beq equipment & technology Co, China) connected to a dry air source. A detailed schematic of the process of the hot corrosion test is shown in Fig. 1. The substrate and coating samples were first weighed and then preheated to approximately 100 ℃ on a heated platform. Afterwards, a saturated aqueous sodium chloride solution is sprayed onto the sample surface to form a uniform salt layer. This process was repeated to ensure that each sample was covered with approximately 3 mg/c㎡ of NaCl.

　　文中所用到的设备正是安徽贝意克设备技术有限公司生产的BTF-1200 C-III多温区管式炉，我们使用该设备对我的样品进行了耐腐蚀试验，温度550 ℃腐蚀240h。该贝意克设备具有三个温度区域，同时设备较好的稳定性、精准的温控和良好的保温效果，助力我做腐蚀以及氧化实验。在我的整个研究生生活中，贝意克设备一直陪伴着我，该设备购买于2018年，已在实验室服役5年，但设备性能依旧稳定，为我们科研的顺利提供了关键的保障。在此表示感谢!最后希望贝意克越办越好，开发出更多实用高效的设备，为广大的科研工作者再添助力!